Votre application – notre solution : en savoir plus sur les méthodes de préparation d'échantillons dans les industries métallurgiques. Prenez connaissance de nos rapports d'application avec des conseils pour le broyage ou consultez notre base de données sur les protocoles de broyage avec de très nombreux exemples et des indications précises. - Rapports et protocoles de broyage ici en anglais -
The provided sample was ultra-pure selenium. In order to comminute this sample, the Planetary Mono Mill PULVERISETTE 6 classic line was equipped with the 250 ml zirconium oxide grinding bowl and 15 x 20 mm grinding balls were chosen; although we recommend in our technical documents a maximum feed size of 10 mm. The chunks shown in the photo are clearly larger though. For the pre-comminution no technology was available which excluded a contamination. Therefore the sample was added as shown.
After a processing of 5 minutes at a maximum rotational speed (650 r/min), it was assessed and exactly as expected, a fine powder with several, few rough chunks was found. On the photo those are seen next to the coin (comparison of size) and on the lower rim of the photo. These chunks were sorted out and the remaining sample was ground further.
After a total of 11 minutes, a fineness was obtained, which allowed the weighted sample of a representative sample amount of 1 g.
Download the FRITSCH-report as PDF-file
Detailed grinding reports