Votre application – notre solution : en savoir plus sur les méthodes de préparation d'échantillons dans les industries métallurgiques. Prenez connaissance de nos rapports d'application avec des conseils pour le broyage ou consultez notre base de données sur les protocoles de broyage avec de très nombreux exemples et des indications précises. - Rapports et protocoles de broyage ici en anglais -
| Matériau | Input size | Final fineness | No. | |
| Alloy | 1 - 2 mm | <100µm | M0098003 | details |
| aluminium - foil | | <250µm | M002113 | details | |
| aluminium splinters | < app. 30x1mm* | fineness was reached | M002135 | details |
| cast iron | 10x5mm | approx. 100µm | M0097047 | details |
| Cerium oxide/copper oxide (90%/10%) | app. <30µm | sticks heavily!*2 | M002128 | details |
| Copper (resin, sample A) | < 2cm | < 0,25mm | M0097268 | details |
| copper ore | * | < 110µm * | M0099025 | details |
| copper ore | 150µm | 57% < 50µm * | M0098346 | details |
| Fe,Sn,Cu ...-compounds: Cu2O (1), Cu2S (2), SnS (3), FeS2 (4) | 10-100µm | d90 <0,4µm | M090024 | details |
| Ferro tungsten | 2cm | ca. 95%<120µm | M001182 | details |
| Ferro tungsten (75%) | app.2,5cm | approx. 6-8mm | M003102 | details |
| Ferro vanadium | < 8mm | ~ < 300µm | M0097222 | details |
| Ferro vanadium | < 1cm | ~ 300-500µm | M0097144 | details |
| Ferro vanadium | | app. 1mm / app.74%<50µm | M003253 | details | |
| Ferrochrome | < 8mm | 67%< 200µm 93% < 200µm | M0098206 | details |
| Ferrochrome | 4 - 5cm | < 1 - 2cm | M0098195 | details |
| Ferrochrome | 3-4mm | 15% <160µm / 51% < 160µm / 80% <160µm | M004028 | details |
| Ferrochrome | <60mm *1 | < app.30mm | M003042 | details |
| ferrosite | 3cm | 36% < 90µm | M0098385 | details |
| Ferrotitanium (70% titanium) | < 6cm | < ca. 100µm | M0098096 | details |
| Ferrum oxide/chrome oxide | d50 < 8,4µm | d90< 2,4µm / d90< 1,9µm d90< 1,3µm / d90< 1,2µm | M004054-1 | details |
| gold dust | <120µm | flocculating | M002146 | details |
| Hard metal (sintered, WC) | app.<2-3cm | 120-130µm | M0099015 | details |
| hardmetal | 3,5 cm | 5,3% > 180µm 21,5% < 100µm | M0098253 | details |
| Iron (pellets) | <1cm | 100%<75µm 50%<19,6µm | M001156 | details |
| iron ore | 5x5x5mm | 16,86 % > 140 µm | M0098247 | details |
| Iron powder | <60mm*1 | < 1-1,5cm | M002053 | details |
| Iron silicide strips | 8cm | < 0,25mm | M0097249 | details |
| iron slag | 5 x 3cm | approx. 14mm | M0098135 | details |
| Metal (brittle) | < 2cm | 80% < 500µm | M0098186 | details |
| Ore | <5-6cm | < ca. 150µm | M003058 | details |
| Ore sample | <6-8mm | ~96%< 1,12mm*2 | M004136 | details |
| sample A sintered alloy of Ti-Fe-Ni | < 10mm | output:4,35g sieving: 10%<100µm | M002139 | details |
| slag with copper | 3 cm | < 1,5 mm | M0097115 | details |
| slag/Cu-metal | | homogenes Pulver | M003073 | details | |
| Stainless steel (powder) | 70µm | ca. 100µm / ca. 300µm* / 150µm (build flakes) | M0097090 | details |
| Steel granulate | <5-7mm | < ca. 0,5-1mm | M002105 | details |
| Steel turning chips | 40x2mm, 0,1mm thick | <800µm | M070536 | details |
| TiSi2 | powder | d50 <0,5µm | M080288 | details |
| TiSi2, Titansilicid | powder | M090049 | details | |
| Titansilicid | << 1mm | << 1mm | M090115 | details |
| tungsten(VI)oxide WO3 | d90 <22µm*1 | d50 <0,46µm*3 d95<1,0µm | M002245 | details |
| Wolfram-Rhenium | 3 - 4mm | 49.6% > 160µm 37.1% = 63-160µm | M0098115 | details |
| Wolfram/tungsten | 1cm | app. 200-300µm | M0096450 | details |