Votre application – notre solution : en savoir plus sur les méthodes de préparation d'échantillons dans le secteur des matériaux de construction. Prenez connaissance de nos rapports d'application avec des conseils pour le broyage ou consultez notre base de données sur les protocoles de broyage avec de très nombreux exemples et des indications précises. - Rapports et protocoles de broyage ici en anglais -
Purple Moor-Grass – Molinia Caerulea… is a genus of two species of grasses.
For milling purposes, dried and pre-crushed grass was supplied by the customer. Clearly visible are the hard blades of grass.
The requirement of the task was, that the material shall be smaller than 0.2 mm. The prospective customer selected the Variable Speed Rotor Mill PULVERISETTE 14 as the instrument for the job. Complying with this demand, the mill was equipped with a 0.2 mm sieve. The result is not satisfactory. Several blades of grass remained intact in their full length. Due to the centrifugal acceleration of the mill an air current develops, which moves the blades of grass lengthwise through the sieve. The PULVERISETTE 14 was now equipped with various finer sieves and the material processed. The results remained unsatisfactory.
For the optimization of the comminution, a so called beater blade insert is available for this mill. With it long, fibrous particle can be broken down well. The next test was therefore performed with the beater blade and a 1 mm sieve. With it, optically, a pretty good result was achieved here. Now the hope existed, that in a second step, by utilizing a finer sieve the desired end fineness could be achieved.
Is the beater blade with a 0.08 mm sieve inserted, oblong particles are still clearly visible though. For a weighted sample of 300 mg, for the classic analysis, this fineness is sufficient. The right photo shows 300 mg.
The carbon nitrogen analyzers only work with 20 mg net weight though. This immediately raises the question for an even finer prepared sample. The solution was found with the Planetary Micro Mill PULVERISETTE 7 classic line. For tough, elastic materials for example hair, we mostly recommend to use sintered corundum bowls and balls. For the here described application, bowls and balls made of hardened steel were proven to be better though.
For the first test, the base sample (not additionally comminuted), was added into the sintered corundum bowl and milled for 20 minutes. Afterwards the grass had been ground down to a homogenous fine powder. Since the sample amounts which are to be added into the bowl are relatively small, a pre- comminution of the samples with the Variable Rotor Speed Mill and beater blade and a 1 mm sieve are in regards to the representativeness recommended.
In additional tests with the Planetary Ball Mill PULVERISETTE 7 classic line, pre-crushed material was added and the steel grinding set used. After 10 minutes the grass was ground into powder like shown in the photo here. Are 20 mg of this sample weighted in, it safely can be assumed, that a representative sample is added to the measuring instrument.